Micro-CT and FE-SEM enamel analyses of calcium-based agent application after bleaching

Abstract

Objectives

The objective of the present study is to evaluate the effects of casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) on bleached enamel.

Materials and methods

A bleaching agent (35% hydrogen peroxide) was applied, 4 × 8 min on premolar teeth (n = 8). A CPP-ACP paste was applied for 7 days. Prior and post-treatment, microtomography images were obtained and 3D regions of interest (ROIs) were selected, from outer enamel, extending to 110.2-μm depth. CT parameters of structure: thickness (St.Th), separation (St.Sp), and fragmentation index (Fr.I.) were calculated for each (ROI). Data was submitted to paired t tests at a 95% confidence level. The samples were evaluated at 3000 to 100,000 magnification. Quantitative analysis of enamel mineral content was also determined by SEM EDX.

Results

There was a significant increase in structure thickness and calcium content. The phosphorus content increased after bleaching. There was also a decreased separation and fragmentation index on the outer enamel to a depth of 56.2 μm (p < 0.05). There were no changes at 110.2-μm depth for the bleaching CPP-ACP association. A covering layer and decreased spaces between the hydroxyapatite crystals appeared around the enamel prisms, 7 days after the CPP-ACP application.

Conclusions

The application of a CPP-ACP provides a compact structure on the enamel's outer surface, for 7 days, due to calcium deposition. CT parameters seem to be a useful tool for mineralizing and remineralizing future studies.

Clinical relevance

CPP-ACP neutralizes any adverse effects on enamel surface when applied during a week after bleaching and minimizes any side effects of the bleaching treatment due to a more compact structure.