Natural manganese ore catalyst for low-temperature selective catalytic reduction of NO with NH 3 in coke-oven flue gas

Abstract

Different types of manganese ore raw materials were prepared for use as catalysts, and the effects of different manganese ore raw materials and calcination temperature on the NO conversion were analyzed. The catalysts were characterized by XRF, XRD, BET, XPS, H₂-TPR, NH₃-TPD, and SEM techniques. The results showed that the NO conversion of calcined manganese ore with a Mn:Fe:Al:Si ratio of 1.51:1.26:0.34:1 at 450 °C reached 80% at 120 °C and 98% at 180~240 °C. The suitable proportions and better dispersibility of active ingredients, larger BET surface area, good reductibility, a lot of acid sites, contents of Mn⁴⁺ and Fe³⁺, and surface-adsorbed oxygen played important roles in improving the NO conversion.