In situ hydrothermal preparation of mesoporous Fe3O4 film for high-performance negative electrodes of supercapacitors

Publication date: 15 July 2018
Source:Microporous and Mesoporous Materials, Volume 265
Author(s): Ke Jiang, Baolong Sun, Mengqi Yao, Ni Wang, Wencheng Hu, Sridhar Komarneni
A mesoporous Fe3O4 film was prepared as binder-free electrode material for supercapacitors through a facile process that included the hydrothermal electroplating of an Fe/Zn alloy, in situ electrolytic dealloying to remove the Zn template, and oxidation in a water vapor environment. The Fe3O4 film showed a cubic structure and mesoporosity with a specific surface area of 247 m2 g−1. As a negative electrode material, the mesoporous Fe3O4 film delivered a high gravimetric capacity of 221 C g−1 at 1 A g−1, and the gravimetric capacity was maintained at 154 C g−1 even at a high current density of 50 A g−1. In addition, the mesoporous Fe3O4 electrode exhibited very high cycling stability (only 4.7% capacity loss after 10,000 galvanostatic charge–discharge cycles). Electrochemical impedance spectroscopy revealed that the mesoporous Fe3O4 film had excellent conductivity, implying its promising application as a supercapacitor electrode.