Abstract
Purpose
The purpose of this in vitro study was to evaluate the hot chemical etching method on the shear bond strength between zirconia and two resin cements.
Materials and Methods
Sixty zirconia specimens (13 × 7.5 × 2.5 mm3) were prepared and treated as follows: (1) airborne-particle abrasion with 50 μm Al2O3 particles; (2) hot chemical etching for 10 minutes; (3) hot chemical etching for 30 minutes. Sixty composite cylinders of 3 mm diameter and height were prepared and bonded to zirconia specimens, which were divided into subgroups A and B. Group A: cemented with conventional resin cement (Variolink II); group B: cemented with 10-metacryloxydecyl dihydrogen phosphate (MDP) monomer containing resin cement (Panavia SA) after the application of surface treatments. Next, the specimens were stored in 37ºC distilled water for 24 hours. Following water storage, shear bond strength test was performed at a 1 mm/min crosshead speed in a universal testing machine. The statistical analyses were performed with one-way ANOVA and post hoc Tukey tests. p < 0.05 was considered statistically significant.
Results
The results from all of the tested groups exhibited lower shear bond strength values than group II-B and higher shear bond strength values than group I-A (p < 0.05).
Conclusion
The use of the hot chemical etching method for 10 minutes increased the shear bond strength of zirconia ceramics to both conventional and resin cements and seems to be an effective method. The MDP monomer-containing resin cement, Panavia SA, improved the resin bonding of zirconia ceramics when combined with airborne-particle abrasion.
from #ORL-AlexandrosSfakianakis via ola Kala on Inoreader http://ift.tt/1P9emay
via IFTTT Medicine by Alexandros G.Sfakianakis,Anapafseos 5 Agios Nikolaos,Crete 72100,Greece,tel :00302841026182 & 00306932607174
from #Med Blogs by Alexandros G.Sfakianakis via Alexandros G.Sfakianakis on Inoreader http://ift.tt/1PUZw4Q
via IFTTT
from #Med Blogs by Alexandros G.Sfakianakis via Alexandros G.Sfakianakis on Inoreader http://ift.tt/1mgxA3J
via IFTTT
Δεν υπάρχουν σχόλια:
Δημοσίευση σχολίου