Highly crystalline stannite-phase Cu2XSnS4 (X = Mn, Fe, Co, Ni, Zn and Cd) nanoflower counter electrodes for ZnO-based dye-sensitised solar cells

Publication date: 5 March 2017
Source:Journal of Alloys and Compounds, Volume 696
Author(s): Yahong Xie, Chunyang Zhang, Guihua Yang, Jianya Yang, Xiaofeng Zhou, Junbao Ma
Quaternary chalcopyrite sulfide semiconductors Cu2XSnS4 (X = Mn, Fe, Co, Ni, Zn and Cd) are successfully prepared by using a solvothermal method. Crystal structure, elemental composition and morphology of the as-synthesized nanoflowers are characterised using XRD, XPS, EDS, TEM and SEM. Photovoltaic and catalytic performances based on prepared samples as counter-electrode (CE) materials in ZnO-based dye-sensitised solar cells (DSSCs) are investigated based on N719 dye and iodide/triiodide electrolyte. Notably, Cu2XSnS4 (X = Mn, Fe, Co, Ni, Zn, Cd) all show excellent catalytic activity for the reduction of I3⁻ to I⁻ in the electrolyte. In addition, Cu2MnSnS4 and Cu2NiSnS4 are explored as CE materials for DSSCs for the first time. Cu2MnSnS4 and Cu2NiSnS4 exhibit power conversion efficiency values of 6.18% and 6.12%, respectively, which are comparable to the photovoltaic performance of the DSSCs using a Pt CE (6.09%).



http://ift.tt/2gMpVZo