Translucency of IPS e.max and cubic zirconia monolithic crowns

Publication date: Available online 21 February 2018
Source:The Journal of Prosthetic Dentistry
Author(s): Paolo Baldissara, Vinícius Felipe Wandscher, Ana Maria Estivalete Marchionatti, Candida Parisi, Carlo Monaco, Leonardo Ciocca
Statement of problemAlthough several monolithic zirconia ceramics have recently been introduced, the need for improved optical properties remains. The newest cubic-zirconia has been claimed to have optimal translucency characteristics for esthetic restorations.PurposeThis in vitro study evaluated the optical properties of novel cubic ultratranslucent (UT) and supertranslucent (ST) zirconia by comparing them with lithium disilicate (L-DIS) glass-ceramic for the manufacture of monolithic computer-aided design and computer-aided manufacturing (CAD-CAM) molar crowns.Material and methodsThe UT and ST multilayered zirconia and the low-translucency grade L-DIS were milled. Eighty monolithic crowns were made from 2 CAD files, corresponding to thicknesses of 1.0 and 1.5 mm, and subdivided (n=20) into 4 groups: UT1.0, UT1.5, ST1.0, and L-DIS1.5. All groups were shaded using A2 color standard. Translucency of the crowns was measured by total transmission, using a photoradiometer in a dark chamber; furthermore, the contrast ratio was analyzed using a dental spectrophotometer applied to the buccal surface of the crowns. Data were analyzed using the Kruskal-Wallis and post hoc multiple Mann-Whitney U tests with Bonferroni correction (α=.05 divided by the number of tests performed in each set).ResultsWhen the ceramic types were analyzed, using total transmission and contrast methods, they showed significantly different translucency levels: UT1.0>ST1.0>UT1.5>L-DIS1.5 (total transmission P<.001). Contrast ratio evaluation yielded similar results (P≤.006); however, the differences between ST1.0 and UT1.5 were not significant.ConclusionsBoth the ST1.0 and UT1.0 crowns, even at the maximum thickness tested (UT1.5), showed significantly higher translucency than L-DIS. Zirconia translucency was improved by eliminating the tetragonal phase, which is responsible for the toughening effect; thus, further studies are advocated to investigate the mechanical resistance of cubic zirconia.



http://ift.tt/2thtUYz