High Tg, melt processable copolyimides based on isomeric 3,3′ and 4,4′-hydroquinone diphthalic anhydride (HQDPA)

Publication date: 31 January 2018
Source:Polymer, Volume 136
Author(s): Lala Rukh Sidra, Guofei Chen, Nafeesa Mushtaq, Lubo Xu, Xiaoqi Chen, Yantao Li, Xingzhong Fang
To extend the upper operating temperature range of melt processable PIs, two series of end-capped copolyimides based on hydroquinone diphthalic anhydride (HQDPA) isomers were designed by varying the contents of appropriate diamines. Thus, copolyimides PI-(0a∼20a) based on 3,3′-HQDPA were prepared by varying the ratio of rigid 2-(4-aminophenyl)-5-aminobenzimidazole (BIA) and flexible 4,4′-oxydianiline (ODA). The resulting copolyimides demonstrated good properties, such as excellent solubility, high Tg ranging from 328 to 354 °C as determined by dynamic mechanical analyzer (DMA), besides, exhibited good thermal stability based on 5% weight loss temperature (T5%) of 502–514 °C and low melt viscosity in the range of 291–935 Pa·s. Most importantly, PI-20a showed a good combination of low melt viscosity simultaneously with significantly high Tg (328 °C). Furthermore, this system was modified by copolymerization with different feed ratio of 4,4′-HQDPA isomer and produced another series PI-(20a∼20e), that exhibited high Tg in the range of 315–330 °C with T5% of 502–543 °C and minimum complex viscosity in the range of 291–479 Pa·s. All PIs form tough and flexible films that have remarkable tensile strength and moduli in the range of 93–116 MPa and 3.7–4.7 GPa, respectively.

Graphical abstract

http://ift.tt/2CO4RQe