The effect of extended glaze firing on the flexural fatigue strength of hard-machined ceramics

Publication date: Available online 28 June 2018
Source:The Journal of Prosthetic Dentistry
Author(s): Iana Lamadrid Aurélio, Catina Prochnow, Luís Felipe Guilardi, Gabriela Freitas Ramos, Marco Antonio Bottino, Liliana Gressler May
Statement of problemIt is unclear whether an extended glaze firing could improve the long-term mechanical performance of densely sintered CAD-CAM ceramics.PurposeThe purpose of this in vitro study was to analyze the effect of an extended glaze firing on the flexural fatigue strength (FFS) of densely sintered milled (hard-machined) leucite-based (LEU) and lithium disilicate-based (DIS) ceramics.Material and methodsDisks were machined from ceramic blocks and divided into 6 groups (n=20) according to the material, LEU or DIS, and to the applied glaze firing: manufacturer-recommended glaze (G group), extended glaze (EG group), and control/no firing (C group). The surface roughness of the disks was measured before and after firing by using a contact profilometer, and data were compared by paired sample tests. Specimens were submitted to fatigue by using the staircase test design in water (piston-on-3 balls; 500 000 cycles, 20 Hz, and sinusoidal loading). Mean (±SD) FFS values were then calculated and analyzed by using 1-way analysis of variance and post hoc Tukey test (α=.05).ResultsSurface roughness did not change after the firing (P>.05). The highest FFS value in both ceramics was obtained after EG firing (LEU-EG=80.52 ±6.3 MPa; DIS-EG=147.25 ±10.5 MPa), which was statistically superior to G firing (LEU-G=73 ±6.8 MPa, P=.003; DIS-G=134.34 ±15.6 MPa; P=.023) and C group (LEU-C=61.94 ±6.3 MPa; P<.001; DIS-C=134.13 ±17.3 MPa; P=.023).ConclusionsEG firing optimized the biaxial flexural fatigue strength of hard-machined leucite and lithium disilicate ceramics compared with conventional glaze firing.



https://ift.tt/2Kx6ghY