A novel electron-microscopic method for measurement of mineral content in enamel lesions

Publication date: October 2018

Source: Archives of Oral Biology, Volume 94

Author(s): C. Fowler, R.J.M. Lynch, D. Shingler, D. Walsh, C. Carson, A. Neale, R.J. Willson, A. Brown

Abstract

Objective

To assess Scanning Electron Microscopy in Back-Scattered Emission mode (BSE-SEM) for measurement of lesion mineral content as a function of depth. Direct comparison is made with Transverse Micro-Radiography (TMR) and Surface Micro-Hardness (SMH) on carious and erosive lesions.

Design

Caries lesions prepared from sound bovine enamel at 37 °C and pH 4.6 in unsaturated (7d) or part-saturated (8d, 4.1 mM Ca²⁺, 8 mM Pi) lactic acid /methyl cellulose gel system, followed by TMR analysis. Erosive lesions prepared from sound bovine enamel (1% citric acid, pH3.8, room temperature) for 5, 10, 15 or 20 min at n = 10 per treatment group. SMH readings (Vickers diamond, 1.9 N, 20 s) were taken from acid-treated and reference areas of each sample. BSE-SEM performed on polished cross-sections of lesioned samples (Jeol JSM6490LV SEM; high vacuum, 10 keV beam voltage, magnification x500 with constant working distance of 10 mm). Under identical SEM conditions, polished standards i.e. MgF₂, alumina, Mg, Al and Si provided a calibration plot of BSE-SEM signal vs. atomic number (z¯). Mineral content vs. depth plots were derived from the cross-sectional BSE-SEM data.

Results

Cross-sectional BSE-SEM images clearly differentiate between caries and erosive lesions. Comparison of caries lesion mineral loss from BSE-SEM with TMR data showed good correlation (R² = 0.98). Similarly, comparison of BSE-SEM data from erosive lesions showed good correlation (R² = 0.99) with hardness loss data from SMH.

Conclusion

BSE-SEM provides a relatively rapid and cost-effective method for the assessment of mineral content in demineralised tooth enamel and is applicable to both caries and erosive lesions.

https://ift.tt/2KHPnBx